Mastercoat® Chassis Coating is a one part urethane coat with extreme chip resistance, very high gloss protective paint which also doesn't leave brush marks. You can apply this coating directly over your wire brushed rust, however for maximum results, we recommend you prime with Mastercoat Silver Primer first. This is the perfect coating for your frames, firewalls, chassis etc. Chassis Black can also be sprayed. Please note, this coating is not UV stable and should only be used where it won’t be exposed to direct sunlight. eg firewalls, frames, Chassis etc.   For a UV stable paint, please use our AG111

  Master Series Chassis Coating 1 US Quart $73

 

 

Technical details.

 
DESCRIPTION  One part aromatic urethane moisture cured finish for frames and floor pans.

COLOR  High gloss black.

PACKAGING  1 US Quart tin. MasterSeries Custom Chassis Black provides a chassis coating that is very durable, corrosion resistant, and has a high degree of chemical and solvent resistancy and extremely high chip resistancy. MasterSeries Custom Chassis Coating can be brushed on with nylon paint brushes and will not leave brush marks.

USES   MasterSeries Custom Chassis Coating is recommended for frames, firewalls, engine components, trunk compartments, and floor pans inside and out.

SURFACE PREPARATION    Previously painted and rusted surfaces for optimum surface preparation, sandblasting is recommended. Apply two coats MasterSeries silver permanent rust sealer/primer. If sandlbasting cannot be done, scrape/wirebrush all loose paint and heavy rust and apply two coats of MasterSeries silver rust sealer as per container directions and top coat with MasterSeries Chassis Coating. MasterSeries Chassis Coating can be directly applied over tightly adherent rust, but the use of MasterSereies silver primer will extend the service life 20 to 25 years.

RECOMMENDED THINNERS  MCT 101


REDUCTION   5% for spray applications if needed.

RECOMMENDED # OF COATS   2 coats.


RECOAT TIME    3 hours minimum. 48 hours maximum.

DRYING TIME - Hard dry 3 hours

Note: When recoating after 48 hours, scufff with 220 grit paper to ensure intercoat adhesion.

APPLICATION    MasterSeries may be applied by brush, roller (short nap) or spray (atomizing or airless). These coatings are moisture curing and it is extremely important that the surface be free of all moisture prior to coating application. Also the coating should dry for a minimum of one hour at 23 degrees C prior to being subjected to moisture (rain); longer at lower temperatures and relative humidity.

Custom Chassis Coating should be stirred for a minimum of 2 minutes. This ensures the carbon black pigment will flow out smoothly. If grittiness occurs, keep stirring the container until grittiness is dissolved.
NEW METAL SURFACES
    New metal surfaces should be sandblasted for optimum adhesion. This is to provide an anchor pattern and to remove mill scale from hot rolled steel. Where sandblasting cannot be done, the use of an acid based metal prep is recommended. Scuff new metal with 220 grit sandpaper to ensure maximum adhesion.

SOLVENT RESISTANCY
    After curing for 7 days at room temperature, MasterSeries Chassis coated panels were subject to various solvents and found to be extremely resistant. After 30 days exposure there was no failure or noticable attack by solvents such as xylol, toluol, or other aromatics. Alcohols and glycols showed no attack. Also, ester solvents such as ethyl glycol acetate had no effect. Acetone softened the film after 10 days, although it hardened upon removal. Methylene chloride destroyed the film in two days. Gasoline, diesel fuel, and JP-4 jet fuel had no effect on the coating.

 

IMPORTANT   Clean equipment immediately after use. If coating is allowed to harden on equipment, an indusrial paint stripper is required to remove it.

PRECAUTIONS   Contains aromatic polyisocyanate prepolymer. Use adequate ventilation, in confined areas, use adequate forced ventilation during application and drying. When spraying, a fresh air mask should be used. Harmful or fatal if swallowed. If swallowed, do not induce vomiting. Call physician immediately.

SUNLIGHT SENSITIVITY   MasterSeries Custom Chassis Coating (black) is sunlight sensitive. It is not recommended for areas exposed to sunlight such as wheels, bumpers, and outer body. For areas exposed to sunlight, AG 111 is recommended.  MASTERSERIES CHASSIS BLACK IS NOT RECOMMENDED FOR AREAS EXPOSED TO DIRECT SUNLIGHT. USE AG 111 BLACK FOR THIS APPLICATION.

SPECIAL BRUSHING INFORMATION:  APPLICATION TEMPERATURE SHOULD BE ABOVE 50 DEGREES  APPLY IN THIN COATS. HEAVY COATS WILL RESULT IN BUBBLING.  CLEAN BRUSHES WITH URETHANE REDUCER IF BRUSHMARKS OCCUR.


PERSISTANT BRUSHMARKS: REDUCE BLACK 5% WITH REDUCER.


CAUTIONS

DIFFICULT TO REMOVE FROM SKIN. Wear gloves and protective clothing. Moisture in skin will cause rapid curing. The use of gloves cannot be overstated.

COMBUSTIBLE

Keep away from heat, sparks, and open flame. Refer also to Material Safety Data Sheet.

WARNINGS: Keep out of reach of children. Harmful or fatal if swallowed. Vapor harmful. Use with adequate ventilation. Avoid contact with skin. Combustible. Keep away from heat and open flame. Close container after use. Avoid contact with eyes and skin. In case of eye contact flush immediately with plenty of water for 15 minutes. CALL A PHYSICIAN. In case of skin contact wash thoroughly with soap & water.

COMBUSTIBLE. Use only with adequate ventilation. Wear a vapor/particulate respirator during application and until work area has been exhausted of all vapor and spray mist. Individuals with chronic respiratory problems or prior respiratory reactions to isocyanates must not be exposed to vapors or spray mist containing isocyanates. If affected by inhalation of vapor or spray mist, remove to fresh air. If breathing difficulty persists or occurs later, consult a physician and have label information available.

CONTAINS AROMATICPOLYISOCYANATE PREPOLYMER, MAY CAUSE LUNG IRRITATION AND ALLERGIC RESPIRATORY REACTION.